Burgman Bellow Mechanical Seal with Sic Seal Faces

• Customization: Available
• Material: Silicon Carbide
• Application: Pump Components
• Type: Rotary Seal/Stationary Seal
• Performance: Sealing Faces
• Shape: O-Ring
• Standard: Nonstandard
• Density: Standard
• Size: as The Client′s Require
• Hardness: Standard
• Flexural Strength: Standard
• Original: China
• Compressive Strength: Standard
• Brand: Junty or as The Client′s Require
• Elastic Modulus: Standard
• Transport Package: Standard or as The Client′s Require
• Specification: SIC, RBSIC, SSIC, SIC+C
• Trademark: Junty or As the client′s require
• Origin: China
• HS Code: 6914900000
• Production Capacity: 5, 000, 000/Month

Product Description

Silicon Carbide (SiC) is one of the most popular high performance tribo-materials, which has been commercially available for more than twenty-five years. Its features include:

· Excellent abrasion and wear resistance
· Excellent corrosion resistance
· Low coefficient of friction
· Low coefficient of thermal expansion
· High thermal conductivity
· Hardness greater than Tungsten Carbide

Different grades of Silicon Carbide are available as following:
· Reaction Bonded Silicon Carbide (RB SiC) - a very economical material which gives excellent wear characteristics, as well as good chemical resistance.
· Sintered Silicon Carbide (SSiC) - the absence of free silicon makes it most resistant to chemically-aggressive fluids, and ideal for high temperature applications.
· Graphite-Loaded Silicon Carbide - this is a composite of silicon carbide and free graphite. Graphite is added to RB SiC (RB SiC + C) or SSiC (SSiC + C), to improve tribological behavior by enhanced lubricity.
 

Parameter	Unit	RB SiC	SSiC
Density	g/cm^3	3.0 - 3.05	3.1
Free Silicon Content	-	12%	-
Crystal Size	µm	8 - 20	5 - 7
Hardness	Rockwell	HRA 90	HRA 93
Compressive Strength	MPa	2700	3000
Flexural Strength	MPa	400	400
Fracture Toughness	MPa	4.3	4.5
Elastic Modulus	GPa	390	410
Poisson's Ratio	-	0.15	0.15
Coefficient of Thermal Expansion	1 x 10^-6 / K	4.3	4.3